Highly ordered mesoporous NiMoO4material was successfully synthesized using mesoporous silica KIT-6 as hard template via vacuum nanocasting method. The structure was characterized by means of XRD, TEM, N2adsorption-desorption, Raman and FT-IR. The mesoporous NiMoO4with the coexistence of α-NiMoO4and β-NiMoO4showed well-ordered mesoporous structure, a bimodal pore size distribution and crystalline framework. The catalytic performance of NiMoO4was investigated for oxidative dehydrogenation of propane. It is demonstrated that the mesoporous NiMoO4catalyst with more surface active oxygen species showed better catalytic performance in oxidative dehydrogenation of propane in comparison with bulk NiMoO4.
SBA-15 supported Mo catalysts(Moy/SBA-15) were prepared by an ultrasonic assisted incipient-wetness impregnation method. The physical and chemical properties of the catalysts were characterized by means of N2-adsorption-desorption, XRD, TEM, UV-Vis, Raman, XANES and H2-TPR. The results showed that a trace amount of MoO3 was produced on high Mo content samples. Turn-over frequency(TOF) and product selectivity are dependent on the molybdenum content. Both Mo0.75/SBA-15 and Mo1.75/SBA-15 catalysts give the higher catalytic activity and the selectivity to the total aldehydes for the selective oxidation of C2H6. At the reaction temperature of 625℃, the maximum yield of aldehydes reached 4.2% over Mo0.75/SBA-15 catalyst. The improvement of the activity and selectivity was related with the state of MoOx species.