The novel material of photonic crystal makes it possible to control a photon, and the photonic integration will have breakthrough progress due to the application of photonic crystal. It is based on the photonic crystal device that the photonic crystal integration could be realized. Therefore, we should first investigate photonic crystal devices based on the active and the passive semiconductor materials, which may have great potential application in photonic integration. The most practical and important method to fabricate two-dimensional photonic crystal is the micro-manufacture method. In this paper, we summarize and evaluate the fabrication methods of two-dimensional photonic crystal in near-infrared region, including electron beam lithography, selection of mask, dry etching, and some works of ours. This will be beneficial to the study of the photonic crystal in China.
A photonic crystal vertical-cavity-surface-emitting laser (PC-VCSEL) with a wavelength of about 850 nm was realized. The direct-current electrically-driven PC-VCSELs with a minimum threshold current of 2 mA and a maximum threshold current of 13.5 mA were obtained. We fabricated a series of PC-VCSEL chips whose lattice constants are in the range from 0.5 to 3 μm with different filling factors, and found that the laser characterization depends on the lattice constant, the filling factor, the size of cavity, etc.
XU XingSheng WANG ChunXia SONG Qian DU Wei HU HaiYang ZHAO ZhiMin LU Lin KAN Qiang CHEN HongDa
This paper reports that a two-dimensional single-defect photonic crystal waveguide in the Γ -K direction with triangular lattice on a silicon-on-insulator substrate is fabricated by the combination of electron beam lithography and inductively coupled plasma etching. A ministop band (MSB) is observed by the measurement of transmission characteristics. It results from the coupling between the two modes with the same symmetry, which is analysed from the stimulated band diagram by the effective index and the two-dimensional plane wave expansion methods. The parameter working on the MSB is the ratio of the radius of air holes to the lattice constant, r/a. It is obtained that the critical r/a value determining the occurrence or disappearance of MSB is 0.36. When r/a is larger than or equal to 0.36, the MSB occurs. However, when r/a is smaller than 0.36, the MSB disappears.