The mold filling and solidification process of a marine propeller hub were simulated using ProCAST. Three casting processes–gravity casting, centrifugal casting and low pressure casting–were compared in order to get the best process. The heat transfer coefficient of the casting/mold interface was determined using a reverse method. The simulated results of velocity, temperature and shrinkage porosity distribution were discussed in detail for the three casting processes. A smooth filling was found in all three casting processes, especially the low pressure casting exhibiting a better filling performance than the other two, but the solidification processes were different. The casting did not experience the sequential solidification, and the feeding paths were blocked, leading to shrinkage porosity defects in the riser and the bottom of the casting in gravity casting and in the upper zone of the casting in low pressure casting. While, the sequential solidification was well controlled in the solidification process of centrifugal casting, and majority of the shrinkage porosity defects can only be observed in the riser. It could be concluded that the centrifugal casting process is the most suitable casting process for the production of propeller hub body. The casting experiments verified the simulation results, and a defect-free propeller hub was obtained by centrifugal casting with a rotational speed of 150 r·min-1.
Wang TongminLi JiaWu LiJie JinchuanCao ZhiqiangKang Huijun
Separation of primary Si phase and removal of boron in the primary Si phase during the solidification process of the Al-30%Si-10%Sn melt under a traveling magnetic field(TMF) were investigated. The results showed that the agglomeration layer of the primary Si can be formed in the periphery of the ingot while the inner microstructures mainly consist of the eutectic α-Al+Si and β-Sn phases. The intense melt flow carries the bulk liquid with higher Si content to promote the growth of the primary Si phase which is first precipitated close to the inner wall of crucible with a relatively lower temperature, resulting in the remarkable segregation of the primary Si phase. The content of impurity B in the primary Si phase can be removed effectively with an increase in magnetic flux intensity. The results of electron probe microanalysis(EPMA) clearly indicated that the average intensity of the B Ka line in the α-Al phase region of Al-Si-Sn alloy is higher in the case of solidification under TMF than that of normal solidification condition, suggesting that the electromagnetic stirring can promote the B removal from the primary Si phase.
The three dimensional(3D) microstructures of Al-Bi alloys with different grain refiners(Al-5Ti-B, Al-3B and Al-3Ti) have been studied using synchrotron X-ray microtomography. The relationships between the microstructures and the corresponding wear behavior are verified through the friction and wear tests. The worn surfaces of the samples with grain refiners tested under 15 and 60 N loads are analyzed using Scanning Electron Microscopy(SEM). The results indicate that the addition of grain refiners is beneficial to the size and distribution of the Bi-rich particles in Al-Bi alloys. Compared with Al-5Ti-B and Al-3B grain refiners, the Bi-rich particles are more uniformly distributed and spherical with finer size with the addition of Al-3Ti grain refiner. The refinement renders the Al-20wt%Bi alloy refined by Al-3Ti the superior wear resistance with respect to those refined by Al-5Ti-B and Al-3B grain refiners, corresponding to the microstructures with fine and uniformly distributed Bi-rich particles in the Al matrix.
WANG TongMinCAO FeiCHEN ZongNingKANG HuiJunZHU JingFU YaNanXIAO TiQiaoLI TingJu
The coarsening process of second-phase droplet in solidifying Al-20 wt% Bi immiscible alloy is in situ studied using synchrotron radiation imaging technology.The collision-induced coarsening and Ostwald coarsening phenomena are directly observed and analyzed.It is found that through observation,collision-induced coarsening phenomenon occurs between droplets with little difference in radius,while Ostwald coarsening phenomenon occurs among droplets with much difference in radius.Moreover,the coarsening rate of Ostwald coarsening is much higher than that of collision-induced coarsening.
Hui-Jun KangPeng ZhouFei CaoJing ZhuYa-Nan FuWan-Xia HuangTi-Qiao XiaoTong-Min Wang