Response surface methodology(RSM)was employed to optimize the control parameters of TiO_(2)/graphene with exposed{001}facets during synthesis,and its enhanced photocatalytic activities were evaluated in the photodegradation of toluene.Experimental results were in good agreement with the predicted results obtained using RSM with a correlation coefficient(R^(2))of 0.9345.When 22.06 mg of graphite oxide(GO)and 2.09 mL of hydrofluoric acid(HF)were added and a hydrothermal time of 28 h was used,a maximum efficiency in the degradation of toluene was achieved.X-ray diffraction(XRD),transmission electron microscopy(TEM),and scanning electron microscopy(SEM)were employed to characterize the obtained hybrid photocatalyst.The electron transferred between Ti and C retarded the combination of electron–hole pairs and hastened the transferring of electrons,which enhanced the photocatalytic activity.
Yifei WangZhiyang ZhangQianqian ShangXin TanHongmei Wang
An efficient visible-light-responsive BiOBr/TiO2 heterojunction nanocomposite was fabricated successfully using in-situ depositing technique at room temperature by introducing BiOBr onto the surface of TiO2 nano- belts pre-prepared by hydrothermal reaction and etched with H2SO4. The obtained particles were characterized by XRD, SEM, TEM, XPS, UV-Vis DRS and PL techniques. BiOBr/TiO2 heterojunction nanocomposites with different mass ratios of m （BiOBr）/m （TiO2） were discussed in order to get the best photocatalytie activity, and BiOBr/TiO2-1.0 was proved to be the optimal mass ratio. BiOBr/TiO2-1.0 exhibited excellent photocatalytic activity in the degradation of RhB compared with TiO2 nanobelts, pure BiOBr and the mechanical mixture of TiO2 nanobelts and BiOBr. At last, a possible mechanism ofphotocatalytic enhancement was proposed.