By using a sol-gel clue, a set of polycrystalline perovskite samples La1-xAgxMnO3 with a nominal doping level x ranging from 0.05 to 0.45 has been synthesized. The chemical composition and the magnetism of the samples were investigated. A little Ag was： found seeping from the samples in the sintering process when the doping level exceeded 0.05 and the sintering temperature was higher than 700℃ resulting in the samples being in multiphase. The magnetic transition points of the samples have been found to decrease with increasing sintering temperature. A concentration-dependent Tc similar to that of bivalent metal ion doped perovskite, has been obtained. We believe that the Ag seeping in the sintering process is responsible for those magnetic characteristics.