Photoluminescence (PL) of Bi12GeO20 and Mo doped Bi12GeO20 (Mo: Bi12GeO20) crystals in visible and near-infrared (NIR) spectral regions were studied. X-ray diffraction analysis, absorption and Raman scattering spectra of these crystals were also measured. Pure Bi12GeO20 after annealing in N2 atmosphere at 450 oC and 550 °C show predominant emissions at about 745 and 1250 nm bands, while the emission peaks of Mo:Bi12GeO20 crystals untreated or after annealing in Ar at 300 °C are at around 538 and 1165 nm. The results suggest that annealing induces intrinsic luminescence of Bi in pure Bi12GeO20 at room temperature and Mo influences the luminescence centers of Bi12GeO20. The emission peaks of Bi12GeO20 and Mo: Bi12GeO20 probably owe to lower-valent Bi ions.
YU PingShengSU LiangBiTANG HuiLiGUO XinZHAO HengYuYANG QiuHongXU Jun
Nd-doped PbWO4 crystals are grown by using the modified Bridgman method.The spectroscopic properties of the crystals are investigated.The changes of the absorption band at 350 nm are discussed for samples annealed at 740℃ and 1040℃.The radiative lifetime of the 4 F 3/2 level is calculated by using the Judd-Ofelt theory according to the absorption spectrum of 0.5 at.% Nd-doped PbWO 4 crystal.The spontaneous Raman scattering properties of the crystals are analysed.