The effects of magnetic field intensity,roasting temperature and roasting time on digestion rate and settling performance of bauxite with different iron contents were investigated systematically.The results indicate that such magnetic treatment can profoundly change the microstructure and digestion performance of bauxite.For the two samples carrying different iron contents,phase transformation of the aluminum oxide phase proceeds faster in the high iron bauxite than the low one.The optimal pretreatment conditions of low iron bauxite are roasting temperature 550 °C and magnetic field intensity 6 T,while for high iron bauxite are 500 °C and 9 T.The digestion rate of alumina can reach 95% and 92% at digestion temperature of 190 °C and 250 °C.The settling performances of roasted ore by intense magnetic field after digestion are enhanced through pretreatment.
The effects of pyrolysis mode and pyrolysis parameters on Cl content in alumina were investigated, and the alumina products were characterized by XRD, SEM and ASAP. The experimental results indicate that the spray pyrolysis efficiency is higher than that of static pyrolysis process, and the reaction and evaporation process lead to a multi-plot state of the alumina products by spray pyrolysis. Aluminum phase starts to transform into γ-Al2O3 at spray pyrolysis temperature of 600 °C, which is about 200 °C lower than that of static pyrolysis process. The primary particle size of γ-Al2O3 product is 27.62 nm, and Cl content in alumina products is 0.38% at 800 °C for 20 min.
To extract vanadium in an environment friendly manner,this study focuses on the process of leaching vanadium from vanadium slag by high pressure oxidative acid leaching.Characterizations of the raw slag,mineralogy transformation,and the form of leach residues were made by X-ray diffraction,scanning electron microscopy,and energy dispersive X-ray spectroscopy.The result shows that the vanadium slag is composed of major phases of fayalite,titanomagnetite,and spinel.During the high pressure oxidative acid leaching process,the fayalite and spinel phases are gradually decomposed by sulfuric acid,causing the release of vanadium and iron in the solution.Meanwhile,unreacted silicon and titanium are enriched in the leach residues.With the initial concentration of sulfuric acid at 250 g·L^(-1),a leaching temperature of 140℃,a leaching time of 50 min,a liquid-solid ratio of 10:1 mL·g^(-1),and oxygen pressure at 0.2 MPa,the leaching rate of vanadium reaches 97.69%.
Guo-quan ZhangTing-an ZhangGuo-zhi LüYing ZhangYan LiuZhuo-lin Liu
Oil-water separation is critical to solvent extraction process of rare earth, which can directly affect the yield and quality of the product. The experiments measure the two-phase separation time in a beaker, mixing uniformity of two phases in the mixer and the oil phase entrainment at oil exit by the Karl Fischer method and numerical simulation for the mixersettler to study the combined effect of gravity and stirring. Experimental results show that relative to the static situation, the separation efficiency resulted from low-speed stirring is increased by 25%. The water content in the oil is a minimum at an offset distance L of 10 cm and the clearance off the tank bottom z of 10 cm is as low as 0.49%. Distribution images of oilwater separation at 2 s indicates that stirring is very conducive to the separation of the oil-water phase.
Wang ShuchanZhang Ting'anZhang ZimuLü ChaoZhao QiuyueLiu Yan
The process of pressure leaching the converter vanadium slag with waste titanium dioxide without roasting was studied. Mineralogy analysis indicates that the converter vanadium slag contains mainly three mineral phases:magnetite, titanium magnetite, and silicate phase. Vanadium is in combination with iron, titanium, manganese,aluminum, and silicon. The impacts of leaching temperature, leaching time, stirring speed, liquid-to-solid ratio, and initial leaching agent concentration were investigated on the waste titanium dioxide leaching process. The results indicate that under the optimal conditions, the vanadium and the iron leaching rates are 96.85 % and 93.50 %, respectively,and the content of titanium is 12.6 % in the residue. The main mineral phases for the residues under the optimal operation conditions are quartz, ilmenite, anatase, and silicate phase, and the residues can be reused as the extraction of titanium raw materials for titanium dioxide production technology by the sulfate method.
Guo-Quan ZhangTing-An ZhangYing ZhangGuo-Zhi LvYan LiuZhuo-Lin Liu