Corrosion behavior of AZ91 magnesium alloy under NaCl particle deposition condition was investigated by gravimetric method and surface analysis technique.It was found that the mass gain increased rapidly at the beginning of exposure and then slowly with time.The corrosion morphologies were observed and the results showed that NaCl deposition resulted in the occurrence of localized corrosion.The composition of corrosion product was analyzed using X-ray photo electron spectroscopy.It was suggested that the corrosion product was a mixture of oxide and hydroxide of magnesium and aluminum.
Corrosion behavior of AZ91 magnesium alloy in simulating acid rain under wet-dry cyclic condition was investigated.The results show that corrosion potential shifts positively and the corrosion current density decreases at low wet-dry cyclic time.Further increase of the cyclic time results in the negative movement of corrosion potential and the increase of current density.SEM observation indicates that corrosion occurs only inαphase,βphase is inert in corrosive medium,and the corrosion of AZ91 magnesium appears in uniform characteristic.XPS analysis suggests that the corrosion product is mainly composed of oxide and hydroxide of magnesium and aluminum,and a small amount of sulfate is also contained in the film.