A very long wavelength infrared(VLWIR) focal plane array based on In As/Ga Sb type-Ⅱ super-lattices is demonstrated on a Ga Sb substrate. A hetero-structure photodiode was grown with a 50% cut-off wavelength of 15.2 μm, at 77 K.A 320×256 VLWIR focal plane array with this design was fabricated and characterized. The peak quantum efficiency without an antireflective coating was 25.74% at the reverse bias voltage of-20 mV, yielding a peak specific detectivity of 5.89×1010cm·Hz^(1/2)·W^(-1). The operability and the uniformity of response were 89% and 83.17%. The noise-equivalent temperature difference at 65 K exhibited a minimum at 21.4 mK, corresponding to an average value of 56.3 mK.
In this paper we focused on the mask technology of inductively coupled plasma(ICP) etching for the mesa fabrication of infrared focal plane arrays(FPA).By using the SiO_2 mask,the mesa has higher graphics transfer accuracy and creates less micro-ripples in sidewalls.Comparing the IV characterization of detectors by using two different masks,the detector using the SiO_2 hard mask has the R_0A of 9.7×10~6 Ω·cm^2,while the detector using the photoresist mask has the R_0A of3.2 × 10~2 Ω·cm^2 in 77 K.After that we focused on the method of removing the remaining SiO_2 after mesa etching.The dry ICP etching and chemical buffer oxide etcher(BOE) based on HF and NH4 F are used in this part.Detectors using BOE only have closer R_0A to that using the combining method,but it leads to gaps on mesas because of the corrosion on AlSb layer by BOE.We finally choose the combining method and fabricated the 640×512 FPA.The FPA with cutoff wavelength of 4.8 μm has the average R_0A of 6.13 × 10~9 Ω·cm^2 and the average detectivity of 4.51 × 10~9 cm·Hz^(1/2).W^(-1)at 77 K.The FPA has good uniformity with the bad dots rate of 1.21%and the noise equivalent temperature difference(NEDT) of 22.9 mK operating at 77 K.
In this paper,we demonstrate bias-selectable dual-band short-or mid-wavelength infrared photodetectors based on In_(0.24)Ga_(0.76)As_(0.21)Sb_(0.79)bulk materials and InAs/GaSb type-II superlattices with cutoff wavelengths of 2.2μm and 3.6μm,respectively.At 200 K,the short-wave channel exhibits a peak quantum efficiency of 42%and a dark current density of5.93×10^(-5)A/cm^2at 500 mV,thereby providing a detectivity of 1.55×10^(11)cm·Hz^(1/2)/W.The mid-wave channel exhibits a peak quantum efficiency of 31%and a dark current density of 1.22×10^(-3)A/cm^2at-300 mV,thereby resulting in a detectivity of 2.71×10^(10)cm·Hz^(1/2)/W.Moreover,we discuss the band alignment and spectral cross-talk of the dual-band n-i-p-p-i-n structure.