Microstructure, precipitate and magnetic characteristic of fmal products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy （OM）, transmission electron microscopy （TEM）, and energy dispersive spectrometry （EDS）. The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are narrowed; the precipitates, whose quantity in normalized plate is more than that in hot-rolled plate greatly, are mainly A1N, MnS, composite precipitates （Cu,Mn）S and so on. Normalizing technology with a temperature of 1120 ℃, holding for 3 min, and a two-stage cooling is a most advantaged method to obtain oriented silicon steel with sharper Goss texture and higher magnetic properties, owing to the uniform surface microstructures and the obvious inhomogeneity of microstructures along the thickness. The normalizing technology with the two-stage cooling is the optimum process, which can generate more fine precipitates dispersed over the matrix, and be beneficial for finished products to get higher magnetic properties.
The continuous cooling transformation curve of heat-affected zone （HAZ） of X70 pipeline steel was mea- sured by Gleeble-3500 thermal mechanical simulator, optical microscope （OM） and hardness analysis. The microstructure transformation rule at different cooling rates and solution behaviors of microalloy carbonitride during heating process of simulated specimens were investigated. When the cooling rate changes from 10 to 20 ℃.s-l, microstructures at HAZ are identified as granular bainite, lathy bainite, and quasi-polygonal ferrite. This micro- structure is featured with fine ferrite grains, martensite/ austenite islands dispersed, high-density dislocations, and fine carbonitride particles, resulting in improving the strength and toughness of HAZ. With the cooling rate increasing to above 40 ℃.s-1, the microstructure is pre- dominantly coarse lathy bainite with clear primary aus- tenite grain boundary. While the cooling rate decreases to below 1 ℃.s-1, a fairly small amount of pearlite can be observed at the boundaries. The strength and toughness of HAZ are deteriorated because of coarse grains among these microstructures. Most of microalloy carbonitrides in HAZ could be dissolved in the matrix during heating process. A few of TiN particles existing as residues in the matrix can prevent austenite grain from growing, and then improve the strength and toughness of HAZ.