Biodegradable porous nanocomposite scaffolds of poly（lactide-co-glycolide）（PLGA） and L-lactic acid（LAc） oligomer surface-grafted hydroxyapatite nanoparticles（op-HA） with a honeycomb monolith structure were fabricated with the single-phase solution freeze-drying method.The effects of different freezing temperatures on the properties of the scaffolds,such as microstructures,compressive strength,cell penetration and cell proliferation were studied.The highly porous and well interconnected scaffolds with a tunable pore structure were obtained.The effect of different freezing temperature（4℃,-20℃,-80℃and -196℃） was investigated in relation to the scaffold morphology,the porosity varied from 91.2%to 83.0%and the average pore diameter varied from（167.2±62.6）μm to（11.9±4.2）μm while theσ_（10） increased significantly.The cell proliferation were decreased and associated with the above-mentioned properties.Uniform distribution of op-HA particles and homogeneous roughness of pore wall surfaces were found in the 4℃frozen scaffold.The 4℃frozen scaffold exhibited better cell penetration and increased cell proliferation because of its larger pore size,higher porosity and interconnection.The microstructures described here provide a new approach for the design and fabrication of op-HA/PLGA based scaffold materials with potentially broad applicability for replacement of bone defects.
Intelligent polymers or stimuli-responsive polymers may exhibit distinct transitions in physical-chemical properties, including conformation, polarity, phase structure and chemical composition in response to changes in environmental stimuli. Due to their unique 'intelligent' characteristics, stimuli-sensitive polymers have found a wide variety of applications in biomedical and nanotechnological fields. This review focuses on the recent developments in biomedical application of intelligent polymer systems, such as intelligent hydrogel systems, intelligent drug delivery systems and intelligent molecular recognition systems. Also, the possible future directions for the application of these intelligent polymer systems in the biomedical field are presented.
A new type of polypeptide(poly(-benzyl-L-glutamate)(PBLG))modified hydroxyapatite(HA)/poly(L-lactide)(PLLA)nanocomposites(PBLG-g-HA/PLLA)were prepared by the solvent-mixing method,and their mechanical and thermal properties were investigated.The tensile test showed that the mechanical properties of PBLG-g-HA/PLLA nanocomposites were better than that of PLLA,even a 0.3 wt%content of PBLG-g-HA in the nanocomposites could make the tensile strength 12%higher than that of the neat PLLA sample,and the tensile modulus was about 17%higher than that of the PLLA sample.The thermal gravimetric analysis(TGA)showed that the PBLG-g-HA/PLLA composites have better thermal stability than the PLLA sample.The differential scanning calorimetry(DSC)was used to characterize the effect of PBLG-g-HA on the crystallization of PLLA.The isothermal crystallization behavior showed that the half crystallization time(t1/2)of PBLG-g-HA/PLLA was much shorter than that of the PLLA sample.When the PBLG-g-HA content was 10%,t1/2 was only 18.7 min,while t1/2 of the PLLA sample was 61.4 min.The results showed that the PBLG-g-HA worked as a nucleating agent and enhanced the crystallization speed of PLLA.
