A new nonlinear optical crystal of sodium terbium borate （Na2.67Tb2.11B3O9, Mr = 573.14） was synthesized by solid reaction method. The colorless transparent single crystals were grown from the high temperature solution by employing NaBO2 as flux. The structure was deter- mined by single-crystal X-ray diffraction method. The compound crystallizes in the orthorhombic system, space group Amm2 with a = 5.0744（10）, b = 10.990（2）, c = 6.9078（14） A, V = 385.24（13） A3, Dc = 4.941 g/cm3, F（000） = 250, Z = 2, μ= 9.205 mm-1, the final R = 0.0253 and wR = 0.0610. Its three-dimensional network structure is constructed from isolated BO33-, Na（1）O8, Na（2）O6, Na（3）O6 and Tb（1）O9 polyhedra. Variable-temperature magnetic susceptibility measurements show the compound is paramagnetic （μj = 7.04 μb）. The intensity of the second harmonic generation of Na2.67Tb2.11B3O9 is 2.5 times that of KDP.