YAG(Y3Al5O12) powder was prepared by co-precipitation method.To avoid pH values changing intensely during titration process,the 4 3 NH HCO solution with 4 3 NH NO was used as precipitant solution.The pH change of precipitant solution during titration process,compositions of precursor,phase formation process and morphology of the prepared powder were investigated by means of pH meter,FT-IR,XRD and TEM.The results show that the presence of 4 3 NH NO in 4 3 NH HCO solution is crucial to alleviate the pH change,lower the calcination temperature and meliorate the morphology of YAG powder.The mechanisms were studied in detail.The YAG phase can be obtained at a lower temperature of 900 ℃.The obtained powder,composed of elliptical particles,showed a meliorated morphology.