The mixed matrix membranes(MMMs) were developed by incorporating graphite oxide(GO) flakes functionalized with iron oxide(Fe_3O_4) into Pebax matrix. The Pebax/Fe_3O_4–GO MMMs were used to separate CO_2/CH_4 and CO_2/N_2 gas mixture. The results showed that the MMMs with magnetic alignment presented the better gas separation performance than that of random arrangement of Pebax/Fe_3O_4–GO mixed matrix membranes. The reason was that the Fe_3O_4–GO flakes arranged magnetically in the membrane played a multiple role in improving the performance of MMMs. Firstly, under the action of the magnetic field,the magnetic alignment of Fe_3O_4–GO flakes in Pebax matrix constructed the shorter transfer path for gas molecule, increasing the CO_2 permeability. Secondly, the hydroxyl groups in GO flakes and the presence of Fe_3O_4 have stronger binding force for water, improving the CO_2 solubility selectivity. Thirdly, the better interaction between the magnetic alignment of GO composites and polymer matrix, reduced the interface defects. Especially, the optimum gas separation performance was obtained at the Fe_3O_4–GO flakes content of 3 wt% in Pebax matrix at vertical arrangement with selectivity of 47 and 75 for CO_2/CH_4 and CO_2/N_2, respectively, and CO_2 permeability of 538 Barrer at 0.2 MPa and room temperature.
Weifang ZhuYun QinZhongming WangJianshu ZhangRuili GuoXueqin Li