Microstructure observation and dynamic mechanical analysis were carried out to investigate the precipitation and responding damping behaviors of AZ31 magnesium alloy. All the strain amplitude-dependent damping curves of the aged alloys are located between the curves of solutionized and as-cast alloys, although they have different critical strain amplitudes. The G-L theory is employed to explain the damping mechanism involving the interaction between the dislocation and the precipitated phase. In addition, a damping peak is observed at temperatures close to 330 ℃ for AZ31 magnesium alloy, which is related to the β-MglTA112 phase dissolution.
Diqing WAN Jincheng WANG Gaifang WANG Lin LIN Zhigang FENG Gencang YANG