Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA, XRD, H2-TPR and XPS. The catalytic activity of the CuO/TiO2-SnO2 catalysts was markedly depended on the loading of CuO, and the optimum CuO loading was 8 wt.% （Tloo = 80 ℃）. The CuO/TiO2-SnO2 catalysts exhibited much higher catalytic activity than the CuO/TiO2 and CuO/SnO2 catalysts. H2-TPR result indicated that a large amount of CuO formed the active site for CO oxidation in 8 wt.% CuO/TiO2-SnO2 catalyst.
Kairong Li Yaojie Wang Shurong Wang Baolin Zhu Shoumin Zhang Weiping Huang Shihua Wu
Polythiophene/WO3（PTP/WO3）organic-inorganic hybrids were synthesized by an in situ chemical oxidative polymerization method,and char- acterized by X-ray diffraction（XRD）,transmission electron microscopy（TEM）and thermo-gravimetric analysis（TGA）.The Polythiophene/ WO3 hybrids have higher thermal stability than pure polythiophene,which is beneficial to potential application as chemical sensors.Gas sensing measurements demonstrate that the gas sensor based on the Polythiophene/WO3 hybrids has high response and good selectivity for de- tecting NO2 of ppm level at low temperature.Both the operating temperature and PTP contents have an influence on the response of PTP/WO3 hybrids to NO2.The 10 wt%PTP/WO3 hybrid showed the highest response at low operating temperature of 70-C.It is expected that the PTP/WO3 hybrids can be potentially used as gas sensor material for detecting the low concentration of NO2 at low temperature.
Jing Huan~Yanfei KangTaili YangYao WangShurong Wang
Porous α-Fe2O3 was synthesized by a simple hydrothermal treatment of FeC13 aqueous solution followed by a calcination process. In the synthesis of porous α-Fe2O3, no templates or pore-directing agents were used. The as-prepared porous α-Fe2O3 was further employed as a support for loading Pt nanoparticles. The gas sensing performance of the obtained porous α-Fe2O3-supported Pt to VOCs was investigated. The sensor presented a high response and fast response-recovery characteristic to several VOCs including acetone, ether, methanol, ethanol, butanol and hexanol. Meanwhile, it exhibited a much higher response than the pure α-Fe2O3 at the operating temperature of 260 ℃. The enhanced sensing properties may be related to the unique porous structure of the α-Fe2O3 support and the promoting effect of active Pt nanoparticles for the sensing reactions.