C/C composites with banded structure pyrocarbon were fabricated by fast chemical vapor infiltration（CVI）,with C3H6 as carbon source,N2 as carrier gas,and three-dimensional（3D） 12K PAN-based carbon fabric with high density of 0.94 g/cm3 as preform.Experimental results indicated that the fracture characteristics of C/C composites were closely related to the frequency of high-temperature treatment（HTT） at the break of CVI process.According to the load？displacement curves,C/C composites showed a pseudoplastic fracture after twice of HTT.After three times of HTT,load？displacement curves tended to be stable with a decreasing bending strength at 177.5 MPa.Delamination failure and intrastratal fiber fracture were observed at the cross-section of C/C composites by scanning electronic microscope.Because the content of pyrocarbon and fibers has a different distribution in layers,the C/C composites show different fracture characteristics at various regions,which leads to good toughness and bending strength.