目的研究水热溶液pH值对AZ91D合金基体上珍珠质涂层的成分、形貌、抗腐蚀能力以及细胞相容性的影响。方法使用不同pH条件下(5.8、7、8.8、11.8)的水热反应溶液,在AZ91D基体上水热合成珍珠质涂层。利用XRD、XPS和SEM分析涂层的化学成分以及微观形貌。用电化学测量系统评估材料在模拟体液(Simulated Body Fluid,SBF)中的开路电位和极化曲线。通过细胞计数试剂盒(CCK-8法)和拍摄细胞荧光照片,来检测珍珠质涂层的细胞相容性。结果珍珠质涂层的成分和形貌会随着水热反应溶液pH值的不同而发生明显的变化。电化学腐蚀试验证实,与空白对照试样相比,沉积有珍珠质涂层的样品的OCP值较高,其Jcorr值也减少了近10倍,Ecorr值向正电位方向移动。此外,弱碱性条件下所沉积涂层的耐蚀性最优,其Ecorr(vs.SCE)值提高了0.16V,Jcorr值降低了8.16×10^-5A/cm^2。细胞相容性测试结果表明,珍珠质涂层不具有毒性,珍珠粉原材料为涂层提供的大量骨生长因子,能够促进成骨细胞的增殖。结论采用水热反应法,成功地在AZ91D合金基体上制得珍珠质涂层,该涂层可以有效地改善镁合金在人体中的耐蚀性和生物相容性。
The effect of concentration of hydrogen peroxide （H2O2） on the surface properties of Ni-Cr alloys was studied. Surface roughness and surface morphology of Ni-Cr alloys were evaluated by surface profiler and scanning electron microscopy after being immersed in different concentrations of H2O2 for 112 h. Surface corrosion products of Ni-Cr alloys were analyzed by photoelectron spectrograph after being immersed in 0% and 30% H2O2. The order of increasing surface roughness of Ni-Cr alloys after being immersed in different concentrations of H2O2 was 0〈3.6%〈10%〈30%. As the concentration of hydrogen peroxide increased, the surface roughness of Ni-Cr alloys increased and the surface morphology showed different degrees of corrosion. According to the XPS results, the corrosion products formed on the outmost surface layer of the studied samples are Ni（OH）2 and BeO.