We design and fabricate a 128 × 128 AlGaAs/GaAs quantum well infrared photodetector focal plane array （FPA）. The device is achieved by metal organic chemical vapor deposition and GaAs integrated circuit processing technology. A test structure of the photodetector with a mesa size of 300μm × 300μm is also made in order to obtain the device parameters. The measured dark current density at 77K is 1.5 × 10^-3A/cm^2 with a bias voltage of 2V. The peak of the responsivity spectrum is at 8.4μm,with a cutoff wavelength of 9μm. The blackbody detectivity is shown to be 3.95 × 10^8 （cm · Hz^1/2）/W. The final FPA is flip-chip bonded on a CMOS read-out integrated circuit. The infrared thermal images of some targets at room temperature background are successfully demonstrated at 80K operating temperature with a ratio of dead pixels of less than 1%.